| Properties | Unit | Teat Typical Value | |||
| Total Thickness | μm | 250±10 | |||
| Density | g/cm3 | 1.05 | |||
| Tensile Strength | MD | Mpa | 89 | ||
| TD | 123 | ||||
| Elongation at Break | MD | % | 78 | ||
| TD | 53 | ||||
| Thermo Shrinkage | 85℃ | MD | % | 0.2 | |
| 30min | TD | 0 | |||
| Whiteness | % | 96 | |||
| YI E313 | 0.87 | ||||
| Glossness | 45° | % | 21.4 | ||
| Reflectivity | 450nm | % | 97.01 | ||
| 550nm | 97.21 | ||||
| 650nm | 97.65 | ||||
| Weatherability | High temperature and humidity test（65×90%RH×500hr） | ΔRf(550nm)<2 | |||
| High temperature test（85℃×500hr） | |||||
| Low temperature test（-20℃×500hr） | |||||
| Cold and hot cycle test（-20℃×1hr~85℃×1hr） | |||||
| Uvioresistant yollowing test | ΔRf(550nm)<2 | ||||
| ΔYI<3 | |||||
| Visual Inspection | / | / | One side bright /one side matt | ||
| Remark: MD is the machine direction, TD is the transverse direction | |||||
| *Typical Values are not guaranteed | |||||
Certificate GB/T13542-2009